PA66 Nylon Raw Material Toughened and Fiber-Reinforced 30% Flame Retardant Glass Fiber Reinforced 25% Polyamide

• Feature: Customized
• CAS No.: 32131-17-2
• Material: Polyamide(Nylon 6.66)/PA
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: Glass Fiber Reinforced 25% Polyamide
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Grade: Injection/Extrusion
• Samples: Free
• ODM/OEM: Accept
• Shape: Pelltes
• Quality: Stable
• Transport Package: 25kg/Bag
• Specification: 65*40*15cm
• Trademark: TOPO NEW
• Origin: China
• HS Code: 3902100090
• Production Capacity: 100kgs/Week
• Package Size: 65.00cm * 40.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

PA66 nylon raw material toughened and fiber-reinforced 30% flame retardant glass fiber reinforced 25% polyamide 

Glass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.

It is high strength, high toughness, wear resistance, and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good electrical insulation, good surface smoothness, easy molding, and other advantages.

Material is approved by RoHS compliant and can be widely used in automotive parts, electronic appliances, power tools, gears, mechanical parts, and other fields.

PA66 (F01 )

Product Description					Applications
·PA66					· Injection molding
·  Excellent heat stability					· Good mechanical properties balance
Properties			Test Method		Test Condition		Unit	Typical Values
Physical properties
RELATIVE VISCOSITY			IS0307 IN 96%H2SO4					2.7
Specific Gravity			ISO 1183		23ºC		g/cm3	1.14
Mechanical properties
Tensile Strength			ISO 527		50mm/min		MPa	78
Elongation at Break			ISO 527		50mm/min		%	50
Tensile Modulus			ISO 527		1mm/min		MPa	3200
Flexural Modulus			ISO 178		2mm/min		MPa	2780
Charpy Notched Impact Strength			ISO 179-1eA		23ºC		kJ/m2	6
Thermal properties
Heat deflection temperature			ISO 75		1.80MPa		C	72
Melting Point			DSC		-		C	222
Other properties
Flammability			UL94		-		3.2mm	V2
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to using the material, please consult with TOPO NEW MATERIAL CO., LTD.
Processing Conditions						Range
Melt Temperature						260-280ºC
Mold Temperature						80-100ºC
Pre-Dry needed						100ºC, 4-8h
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines,  mold design, and product design.

Are you a trading company or manufacturer?

We are a manufacturer.

 

About Sample?

A 5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.

How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, and we have professional QC for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? Is the sample free? 

7-10 days to send free samples by DHL, TNT, and UPS.