PA66 Heat Resistant Nylon 66 Resins Engineered Thermoplastics Plastic

• Feature: Retardant Nylon PA66 Granules
• CAS No.: 32131-17-2
• Material: Polyamide(Nylon 6.66)/PA
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Grade: Injection/Extrusion
• Samples: Free
• ODM/OEM: Accept
• Shape: Pelltes
• Quality: Stable
• Transport Package: 25kg/Bag
• Specification: 65*40*15cm
• Trademark: TOPO NEW
• Origin: China
• HS Code: 3902100090
• Production Capacity: 100kgs/Week

Product Description

 PA66 heat resistant nylon 66 resins Engineered Thermoplastics plastic

Glass fiber reinforced nylon PA66 is made of PA66 resin and filled with 10-40% glass fiber.

It is high strength, high toughness, wear resistance, and corrosion resistance. Also, the material is dimensionally stable with high heat deflection temperature, good electrical insulation, good surface smoothness, easy molding, and other advantages.

Material is approved by RoHS compliant and can be widely used in automotive parts, electronic appliances, power tools, gears, mechanical parts, and other fields.

PA66 (F0105 NC)

Product Description					Applications
·PA66					· Injection molding
·  Excellent toughness					· Good mechanical properties balance
Properties			Test Method		Test Condition		Unit	Typical Values
Physical properties
Specific Gravity			ISO 1183		23ºC		g/cm3	1.085
Mechanical properties
Tensile Strength			ISO 527		50mm/min		MPa	53.3
Elongation at Break			ISO 527		50mm/min		%	39.9
Tensile Modulus			ISO 527		1mm/min		MPa	2060
Flexural Strength			ISO 178		80*10*4		MPa	70
Flexural Modulus			ISO 178		2mm/min		MPa	1750
Charpy Notched Impact Strength			ISO 179-1eA		23ºC		kJ/m2	75
Charpy Notched Impact Strength			ISO 179-1eA		-30ºC/4h		kJ/m2	14
Thermal properties
Heat deflection temperature			ISO 75		1.80MPa		ºC	68.1
Heat deflection temperature			ISO 75		0.45MPa		ºC	145
Melting Point			DSC		-		ºC	255
Other properties
Flammability			UL94				1.6mm	HB
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to using the material, please consult with TOPO NEW MATERIAL CO., LTD.
Processing Conditions						Range
Melt Temperature						245-260ºC
Mold Temperature						60-70ºC
Injection Speed						65-80%
Pre-Dry needed						120ºC, 2h
Note: The above process condition is only for reference. The actual process should be adjusted according to different type of machine,  mold design and product design.

Are you a trading company or manufacturer?

We are manufacturer.

 

About Sample?

A 5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.

How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, we have professional QC for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? is the sample free? 

7-10 days to send free samples by DHL, TNT, and UPS.