Transparent Heat-Resistant Toughened PMMA Plastic Raw Material PMMA

• Customization: Available
• Feature: Customized PMMA
• Material: Polymethyl Methacrylate/PMMA
• Model NO.: PMMA plastic raw material
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Sample: Avaiable
• ODM/OEM: Accept
• Glass: 5%-60%
• Form: Pellet/ Grain/ Granule
• Application: Onstruction, Medical Equipment, and Machinery Indu
• Transport Package: 25kg/Bag
• Specification: 65*40*15cm
• Trademark: TOPO NEW
• Origin: China
• HS Code: 3902100090
• Production Capacity: 100kgs/Week
• Package Size: 65.00cm * 40.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

Transparent toughened PMMA plastic raw material PMMA

Polymethyl methacrylate (PMMA), it is commonly known as "organic glass" or "acrylic". It is a polymer obtained by free radical polymerization of methyl acrylate and is a common glass substitute material.
Characteristic:
PMMA has advantages such as high transparency, high strength, low weight, easy mechanical processing, impact resistance, weather resistance, and flame retardancy.
High strength: PMMA has relatively high strength, with 7 to 18 times higher tensile and impact resistance than ordinary glass.
Low density: The density of PMMA is approximately 1.15-1.19g/cm, which is half of glass (2.40-2.80g/cm) and 43% of aluminum (a light metal).
Application:
Widely used in fields such as construction, medical equipment, and machinery industry.

PMMA (TPC211) NA

Product Description		Applications
·Good dimensional stability		· Injection molding
· Excellent heat stability		·Good mechanical properties balance
Properties	Test Method	Test Condition		Unit	Typical Values
Specific Gravity	ISO 1183	23ºC		g/cm3	1.19
MI	ISO 1183			g/10min	14
Ash	ISO 3451	800ºC,30min		%	0
Mechanical properties
Tensile Strength	ISO 527	50mm/min		MPa	68
(Yield) elongation	ISO 527	50mm/min		%	/
Flexural Modulus	ISO 178	2mm/min		MPa	/
Cantilever beam notched impact strength	ISO 180	23ºC		kJ/m2	2
Non-notched impact strength of cantilever beam	ISO 180	23ºC		kJ/m2	/
Other properties
Flammability	UL94	3.2			HB
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to using the material, please consult with TOPO NEW  Material Co., Ltd.
Processing Conditions			Range
Melt Temperature			230-250ºC
Mold Temperature			60-100ºC
Pre-Dry needed			90ºC, 3-4h
Note: The above process condition is only for reference. The actual process should be adjusted according to a different type of machine,  mold design, and product design.

Are you a trading company or manufacturer?

We are manufacturer.

 

About Sample?

A 5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.

How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, and we have professional QC for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? Is the sample free? 

7-10 days to send free samples by DHL, TNT, or UPS.