15% Glass Fiber Plastic Raw Material POM Resin

• Customization: Available
• Feature: POM Polyoxymethylene POM Granules From China Facto
• CAS No.: 24969-26-4
• Model NO.: POM Resin
• Formula: C6h12o5
• EINECS: 200-001-8
• Material: Polyacetal/POM
• Usage: General Plastics, Engineering Plastics, Specialty Plastics
• Plastic Properties After Heated: Thermoplastic Plastics
• Plastic Forming Method: Injection
• Color: White
• Sample: Avaiable
• ODM/OEM: Accept
• Glass: 5%-60%
• Form: Pellet/ Grain/ Granule
• Application: Automobile Industry; Switch
• Transport Package: 25kg/Bag
• Specification: 65*40*15cm
• Trademark: TOPO NEW
• Origin: China
• HS Code: 3907101090
• Production Capacity: 100kgs/Week
• Package Size: 65.00cm * 40.00cm * 15.00cm
• Package Gross Weight: 25.000kg

Product Description

15% glass fiber raw material pom resin

Polyoxymethylene(POM): is also commonly known as (Poly)acetal, POM is a kind of Semi-crystalline Polymers, strong, has nice rigidity, and high mechanical strength, which means it is widely used in different industrial usages. The chemical formula of Polyoxymethylene is (CH2O)n.

 

POM can be divided into homopolymer and copolymer by different manufacturing processes, below please check the comparing properties of them:

• Polyoxymethylene-Homopolymer (POM-H): Also known as Acetal Homopolymer, with higher crystallinity, thus the density, melting temperature, and rigidity are also higher, and the tensile strength is higher as well. POM-H has better mechanical properties, and a shorter molding cycle time, so it can help reduce molding costs and it allows us to use on different mold designs.
• Polyoxymethylene-Copolymer (POM-C): Also known as Acetal Copolymer, which has better resistance to chemical solvents (alkaline environment), it has lower melting temperature, and faster molding cycles, thus it's easier for manufacture processing, furthermore, it has better maintenance of color under UV exposure.

.

 
Features: 

1, POM has a very low coefficient of friction and geometric stability, POM plastic is particularly suitable for the production of gears and bearings.
2, POM has high-temperature resistance, so POM is also used in pipeline devices.
3, POM is a tough and elastic material, POM still has good creep resistance even at low temperatures, and POM has good geometric stability and impact resistance.
4, the high degree of crystallization of POM leads to its high shrinkage, POM plastic can reach 2% to 3.5%. POM has different shrinkage rates for a variety of different reinforced materials.

POM(TYM90)

Product Description		Applications
·Good dimensional stability		· Injection molding
· Excellent heat stability		·Good mechanical properties balance
Properties	Test Method	Test Condition		Unit	Typical Values
Specific Gravity	ISO 1183	23ºC		g/cm3	1.41
MI	ISO 1183			g/10min	9
Ash	ISO 3451	800ºC,30min		%	0
Mechanical properties
Tensile Strength	ISO 527	50mm/min		MPa	63
(Fracture) elongation	ISO 527	50mm/min		%	33
Flexural Modulus	ISO 178	2mm/min		MPa	2500
Mold Shrinkage	Internal test method			ºC	1.8-2.2
Hardness	---			---	75M
Bending Strength	ISO 178	23ºC		MPa	87
Notched Charpy Impact strength	ISO 179/1eA	23ºC		KJ/m2	6
Other properties
Note: The data above is a typical value for reference, not a guaranteed value. The data will vary with tool design such as gate type, gate location, gate number, injection molding process, and part thickness. The data will vary with different colors as well. Prior to using the material, please consult with TOPO NEW  Material Co., Ltd.
Processing Conditions			Range
Melt Temperature			230-250ºC
Mold Temperature			60-100ºC
Pre-Dry needed			90ºC, 3-4h
Note: The above process condition is only for reference. The actual process should be adjusted according to different types of machines,  mold designs, and product designs.

Are you a trading company or manufacturer?

We are a manufacturer.

 

About Sample?

A 5 KG Free Sample can be offered per your request.

 

About Material Color?

We can make the material to your appointed color according to Pantone/RAL#.

How does your factory control the quality?
Quality is the Priority, we always pay great importance to quality from beginning to end, and we have professional QC for item quality from spare parts to finished goods.
 

 How many days for mass production?

20 days after all artwork and 30% deposit are confirmed.
 

 How can I get the samples? Is the sample free? 

7-10 days to send free samples by DHL, TNT, and UPS.